Plasma cutters advices: how to become a better welder and how to pick the best welding equipment. How do I choose what size Tig Welding Rod should I use for the job? For sheet metal up to 1/8” thick, don’t use a welding rod that is bigger than the thickness of metal you are welding…at least not much bigger. A good example…is using a 3/32 rod for welding .040 metal. That will just give you a fit. The amperage is low and the weld puddle needs to be small in order to prevent blowing a hole…and then when you dip the rod into the puddle, the rod is a big heat sink and sucks the heat right out of the puddle making it hard to maintain a consistent size bead. But Beginners should probably not be practicing on really thin metal. If you are a beginner you should be practicing on around 1/8 ” thick metal, and the bigger the rod, the easier it is to feed. For 1/8 ” metal, Use larger diameter rods (3/32” to 1/8”) So here is the rule….thin metal, use a thin rod Thick metal, use a thicker rod. This might seem like a no brainer, but I have answered a lot of questions like this about the rod melting before it gets to the puddle. If torch angle and arc length are right, its usually the rod size.
Extend your Tungsten Electrode out Far enough but not too: Too short of a tungsten stickout from the cup will not let you hold a close enough arc length and will not let you see the tip of your electrode. You need to be able to see the tip of the electrode without getting a kink in your neck in order to keep your arc length right. Some textbooks are just plain wack when they only recommend extending your electrode one tungsten diameter past the end of the TIG cup. Holding too long an arc will not pinpoint the heat well enough and will let your rod ball up and blob into the weld.. but we already covered that didn’t we? I remember a consulting gig once where the welder at the aluminum body truck repair shop could not get the aluminum socket weld to puddle. The only thing wrong was that the electrode was recessed back in the cup. Once I extended it out about 3/8″, Everything was fine. ( I also talked them into getting some helium argon mix.)
First, practice handling the gun without actually welding. Rest its barrel in one hand, and support that hand on the table. The other hand operates the gun’s trigger. Stand in a comfortable position and move the gun steadily over the work surface. Adjust your posture and gun movement so that they feel natural. Attach the work lead to the workpiece, and hold the gun so the wire meets the weld surface at about a 30-degree angle. Touch the wire very lightly to the surface, squeeze the trigger, and gently pull the gun toward you to make your first test weld. The wire should melt off into the weld puddle at an even rate and make a steady crackling noise as you go. Adjust the welder settings if needed.
Looking for the best MIG Welders? We recommend Welding Supplies Direct & Associate company TWS Direct Ltd is an online distributor of a wide range of welding supplies, welding equipment and welding machines. We supply Plasma Cutters, MIG, TIG, ARC Welding Machines and support consumables to the UK, Ireland and Europe.
Keep in mind that heavy-duty MIG welding often produces a lot of heat, sparks and spatter, and requires a lower degree of dexterity than some other forms of welding. Therefore, using thick, stiff leather gloves that provide a higher level of protection is smart. Similarly, choose leather footwear that covers your entire foot and leaves as little room as possible for spatter to fall along your ankle line. High-top leather shoes and work boots often provide the best protection. Finally, always be sure you have adequate ventilation per OSHA recommendations and check material safety data sheets (MSDS) for each metal being welded and filler metal being used. Use a respirator whenever required by the MSDS.